10003 Study of a Failure a Decohesion Failure in a Three Layer Coating of a 24" Gas Pipeline in Veracruz in South East Mexico

Picture for 10003 Study of a Failure a Decohesion Failure in a Three Layer Coating of a 24" Gas Pipeline
Available for download
Product Number: 51300-10003-SG
ISBN: 10003 2010 CP
Author: Lagos, Magana, Lopez, Padilla, Canto, Villamizar, Escalera, Ascencio, and Martinez
Publication Date: 2010
$0.00
$20.00
$20.00
The three layer pipeline coating system is one of the fastest growing and more accepted systems in the world, in great part due to the combination of the excellent adhesion properties of the FBE, and the excellent water impermeability and mechanical resistance of the HDPE. We report a case study of a disbondment failure occurred at a 24” gas pipeline and the steps taken to try to determine the root cause of the failure.

KEY WORDS.- Fusion bonded epoxy, three layer pipeline coating system, cathodic protection shielding, material characterization
The three layer pipeline coating system is one of the fastest growing and more accepted systems in the world, in great part due to the combination of the excellent adhesion properties of the FBE, and the excellent water impermeability and mechanical resistance of the HDPE. We report a case study of a disbondment failure occurred at a 24” gas pipeline and the steps taken to try to determine the root cause of the failure.

KEY WORDS.- Fusion bonded epoxy, three layer pipeline coating system, cathodic protection shielding, material characterization
Product tags
Also Purchased
Picture for 10002 Failure Analysis of Three Layer Polypropylene Pipeline Coatings
Available for download

10002 Failure Analysis of Three Layer Polypropylene Pipeline Coatings

Product Number: 51300-10002-SG
ISBN: 10002 2010 CP
Author: Ali Noor Moosavi, Benjamin T. A. Chang and Kamal Mohamed Morsi
Publication Date: 2010
$20.00

Three layer polypropylene (3LPP) pipeline coatings failed prematurely in the oilfields of Abu Dhabi in the United Arab Emirates (UAE). A failure investigation and analysis into this phenomenon was instigated. The coating disbondment has been found to be due to high residual stress concentration and adhesion loss.
Picture for Fusion Bonded Epoxy Coatings (FBE) and Disbondment
Available for download

Fusion Bonded Epoxy Coatings (FBE) and Disbondment

Product Number: 51316-7246-SG
ISBN: 7246 2016 CP
Author: Mehrooz Zamanzadeh
Publication Date: 2016
$20.00

In this paper, failure analysis methodology will be applied to the principal mechanisms by which FBE coatings fail during long term service; with specific application to case studies involving blistering. The case studies apply standard failure analysis techniques to determine the primary causes and modes of failures.
Picture for 00755 PIPELINE COATING FAILURE - NOT ALWAYS
Available for download

00755 PIPELINE COATING FAILURE - NOT ALWAYS WHAT YOU THINK 1T IS

Product Number: 51300-00755-SG
ISBN: 00755 2000 CP
Author: Dennis Neal
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support