09229 Synthesis and Characterisation of Ni-Al2O3 Composite coating by Electrodeposition Method

Picture for 09229 Synthesis and Characterisation of Ni-Al2O3 Composite coating by Electrodeposition Method
Available for download
Product Number: 51300-09229-SG
ISBN: 09229 2009 CP
Author: Pallav Bhadauria, Venkatraman Hariharan and Dhanashree Aole
Publication Date: 2009
$0.00
$20.00
$20.00
Dispersion strengthened Nickel- alumina composite was fabricated by electro-deposition method on a non-metallic substrate with the help of nickel-sulphamate bath. The fine particles of alumina were dispersed and vigorously stirred in the bath in order to get uniformly into the Ni-matrix. The influencing parameters i.e. current density, pH, and temperature of the electrolyte were varied to study the effect on the composite quality.

The Ni-alumina dispersion strengthened composite was fabricated by optimizing the parameters like current density, temperature, pH of the electrolyte etc. of the sulphamate bath. The composite coatings were characterized pertaining to physical appearance, microstructure, hardness and thickness. The obtained results indicate that the micro-structural refinement of the Ni- matrix and uniformity of distribution of oxide particles is obtained by choosing the small size of (less than 5 µm) particles. Also the results indicate increase in the hardness of the Ni-matrix after dispersion of the oxide particles.

Keywords: Nickel sulphamate solution, electro-deposition method, Nickel coating, alumina particles dispersion, and dispersion strengthening effect
Dispersion strengthened Nickel- alumina composite was fabricated by electro-deposition method on a non-metallic substrate with the help of nickel-sulphamate bath. The fine particles of alumina were dispersed and vigorously stirred in the bath in order to get uniformly into the Ni-matrix. The influencing parameters i.e. current density, pH, and temperature of the electrolyte were varied to study the effect on the composite quality.

The Ni-alumina dispersion strengthened composite was fabricated by optimizing the parameters like current density, temperature, pH of the electrolyte etc. of the sulphamate bath. The composite coatings were characterized pertaining to physical appearance, microstructure, hardness and thickness. The obtained results indicate that the micro-structural refinement of the Ni- matrix and uniformity of distribution of oxide particles is obtained by choosing the small size of (less than 5 µm) particles. Also the results indicate increase in the hardness of the Ni-matrix after dispersion of the oxide particles.

Keywords: Nickel sulphamate solution, electro-deposition method, Nickel coating, alumina particles dispersion, and dispersion strengthening effect
Product tags
Also Purchased
Picture for Accelerated Offshore Coating Performance Testing
Available for download

Accelerated Offshore Coating Performance Testing

Product Number: 51317--9134-SG
ISBN: 9134 2017 CP
Author: Benjamin Chang
Publication Date: 2017
$20.00

Offshore is a very corrosive environment with a high corrosion rate. The offshore coating service life is relatively short and extremely expensive to apply maintenance coatings onsite.  A new accelerated coating corrosion test method is proposed.
Picture for 8X194 Materials & Fabrication Practices Pressure V
Available for download

NACE Publication 8X194-2006-SG, Materials and Fabrication Practices for New Pressure Vessels Used in Wet H2S Refinery Service

Product Number: 24179-SG
ISBN: 8X194 Materials
Publication Date: 2006
$109.00

Materials selection, fabrication, postweld heat treatment, inspection, and testing practices for pressure vessels to reduce the likelihood of low-temperature hydrogen damage in wet H2S environments.
Picture for ANSI/NACE No. 13/SSPC-ACS-1 Industrial Coating and Lining Application Specialist Qualification and C
Available for download

ANSI/NACE No. 13/SSPC-ACS-1-2016, Industrial Coating and Lining Application Specialist Qualification and Certification

Product Number: 21122-SG
ISBN: 1-57590-215-X
Publication Date: 2015
$109.00

Requirements for qualification of an industrial coating and lining application specialist that includes surface preparation and coating application for steel and concrete surfaces of industrial structures.
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support