08572 Erosion-Corrosion in Disturbed Liquid/Particle Flow

Picture for 08572 Erosion-Corrosion in Disturbed Liquid/Particle Flow
Available for download
Product Number: 51300-08572-SG
ISBN: 08572 2008 CP
Author: Joshua Addis, Srdjan Nesic, and Bruce Brown
Publication Date: 2008
$0.00
$20.00
$20.00
Erosion-corrosion occurs in pipelines that transport both corrosive liquids and erosive solid particles. This study has tested the erosion-corrosion behavior of mild carbon steel under conditions where there is no protective iron carbonate film. High and low NaCl concentrations were studied in order to determine the effect of salt concentration on the erosion-corrosion process as well as the individual pure corrosion and pure erosion processes. The effect of erosion-corrosion on mild steel was tested under disturbed flow by using a specially designed test section consisting of three flow alterations: a flow constriction, protrusion, and expansion. Under the tested conditions it was found that there is no synergistic effect between erosion and corrosion and that for an unprotected base metal the rate of metal loss is equal to the sum of erosion loss and corrosion loss. The higher salt concentration led to a lower corrosion rate and erosion rate but did not affect the interaction between erosion and corrosion.
Erosion-corrosion occurs in pipelines that transport both corrosive liquids and erosive solid particles. This study has tested the erosion-corrosion behavior of mild carbon steel under conditions where there is no protective iron carbonate film. High and low NaCl concentrations were studied in order to determine the effect of salt concentration on the erosion-corrosion process as well as the individual pure corrosion and pure erosion processes. The effect of erosion-corrosion on mild steel was tested under disturbed flow by using a specially designed test section consisting of three flow alterations: a flow constriction, protrusion, and expansion. Under the tested conditions it was found that there is no synergistic effect between erosion and corrosion and that for an unprotected base metal the rate of metal loss is equal to the sum of erosion loss and corrosion loss. The higher salt concentration led to a lower corrosion rate and erosion rate but did not affect the interaction between erosion and corrosion.
Product tags
Also Purchased
Picture for Erosion-Corrosion Study of Oilfield Materials Due to Liquid Impact
Available for download

Erosion-Corrosion Study of Oilfield Materials Due to Liquid Impact

Product Number: 51315-6136-SG
ISBN: 6136 2015 CP
Author: Hadi Arabnejad Khanouki
Publication Date: 2015
$20.00

The goal of this work is to determine erosion-corrosion damage caused by liquid impact in the oil and gas industry.

Picture for 98058 EROSION IN MULTIPHASE PRODUCTION OF OIL
Available for download

98058 EROSION IN MULTIPHASE PRODUCTION OF OIL & GAS

Product Number: 51300-98058-SG
ISBN: 98058 1998 CP
Author: Ken Jordan
$20.00
Picture for 03319 EROSION-CORROSION MITIGATION USING CHEMICALS
Available for download

03319 EROSION-CORROSION MITIGATION USING CHEMICALS

Product Number: 51300-03319-SG
ISBN: 03319 2003 CP
Author: A Neville, C Wang, S Ramachandran, V Jovancicevic
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support