08464 High Temperature Gas Corrosion of Fe-Cr-Ni-Al-La Alloy

Picture for 08464 High Temperature Gas Corrosion of Fe-Cr-Ni-Al-La Alloy
Available for download
Product Number: 51300-08464-SG
ISBN: 08464 2008 CP
Author: Olga Tsurtsumia, Elguja Kutelia, Boris Bulia, Omar Mikadze, and Sayavur Bakhtiyarov
Publication Date: 2008
$0.00
$20.00
$20.00
High-chromium (>40%) content Fe-Cr-Ni-Al-La alloy was investigated in different corrosive environment (laboratory air, N2O4, exhaust gas) at various elevated temperatures. Oxidation kinetics, as well as morphology, phase and elemental compositions of the oxide scale developed at the initial oxidation stages were of our interest. It was determined that condition of oxidized surface had defined influence on the process of oxide scale formation at high temperatures; the optimal correlation of preoxidation temperatures enables alloy’s exploitation at 1200-1300OC rather long time owing to the complex composition surface scale with modulated morphology and to its underlying, uniform, continuous alumina layer strongly adhered to metallic matrix. Here, the alumina is responsible for the blocking of ways for cation and anion counter-diffusion at high temperatures. High-chromium Fe-Cr-Ni-Al-La alloy showed rather good stability in the highly corrosive N2O4 environment at 750OC and practically kept its mechanical properties unchangeable. At the temperatures higher then 1300OC it take place a slight creep of the bulk metallic matrix, nevertheless it is still possible can be applied as a coating material for any heat-proof ones in the purpose of increasing the heat and corrosion resistance of underlying substrate making the obtained compositional system effective for utilization around 1400OC.
High-chromium (>40%) content Fe-Cr-Ni-Al-La alloy was investigated in different corrosive environment (laboratory air, N2O4, exhaust gas) at various elevated temperatures. Oxidation kinetics, as well as morphology, phase and elemental compositions of the oxide scale developed at the initial oxidation stages were of our interest. It was determined that condition of oxidized surface had defined influence on the process of oxide scale formation at high temperatures; the optimal correlation of preoxidation temperatures enables alloy’s exploitation at 1200-1300OC rather long time owing to the complex composition surface scale with modulated morphology and to its underlying, uniform, continuous alumina layer strongly adhered to metallic matrix. Here, the alumina is responsible for the blocking of ways for cation and anion counter-diffusion at high temperatures. High-chromium Fe-Cr-Ni-Al-La alloy showed rather good stability in the highly corrosive N2O4 environment at 750OC and practically kept its mechanical properties unchangeable. At the temperatures higher then 1300OC it take place a slight creep of the bulk metallic matrix, nevertheless it is still possible can be applied as a coating material for any heat-proof ones in the purpose of increasing the heat and corrosion resistance of underlying substrate making the obtained compositional system effective for utilization around 1400OC.
Product tags
Also Purchased
Picture for 08454 Stress Relaxation Cracking Of Welded Joints In Thick Sections Of Type-347 Stabilized Grade Of
Available for download

08454 Stress Relaxation Cracking Of Welded Joints In Thick Sections Of Type-347 Stabilized Grade Of Stainless Steel

Product Number: 51300-08454-SG
ISBN: 08454 2008 CP
Author: Christian E. van der Westhuizen
Publication Date: 2008
$20.00

This paper discusses reactors in hydrocarbon service that experienced numerous cracking problems over a 8-year period, where cracks were confined to the welded zones.  The material is  TP347 stainless steel, welded with E347-16 consumables.
Picture for 08447 Influence of Pressure and Chromium Content on Corrosion Reactions at 600C in a CO2-H2O Atmosph
Available for download

08447 Influence of Pressure and Chromium Content on Corrosion Reactions at 600C in a CO2-H2O Atmosphere

Product Number: 51300-08447-SG
ISBN: 08447 2008 CP
Author: Daniela Huenert and Axel Kranzmann
Publication Date: 2008
$20.00
Picture for 08462 SEM and Hot Corrosion Evaluation of 80Ni-20Cr Coating Applying Electrochemical Techniques
Available for download

08462 SEM and Hot Corrosion Evaluation of 80Ni-20Cr Coating Applying Electrochemical Techniques

Product Number: 51300-08462-SG
ISBN: 08462 2008 CP
Author: Cecilia Cuevas-Arteaga, Jesús Porcayo-Calderón, and Segio Serna
Publication Date: 2008
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support