08447 Influence of Pressure and Chromium Content on Corrosion Reactions at 600C in a CO2-H2O Atmosphere

Picture for 08447 Influence of Pressure and Chromium Content on Corrosion Reactions at 600C in a CO2-H2O Atmosph
Available for download
Product Number: 51300-08447-SG
ISBN: 08447 2008 CP
Author: Daniela Huenert and Axel Kranzmann
Publication Date: 2008
$0.00
$20.00
$20.00
Power plant components in Integrated Gasification Combined Cycles (IGCC) and gas turbines work under conditions of high pressure, high temperature and flowing gas with high levels of CO2. The corrosion process occurring under such service conditions of modern power plants is different from that under current conditions with air combustion. The effect of pressure and chromium content on the corrosion reaction of steels at a constant temperature of 600°C (873K) is discussed in the present paper. The flowing gas is simulated as a mixture of 30% H2O und 70% CO2. The influence of chromium contents of 1, 2, 9 and 11% were experimentally observed.
Power plant components in Integrated Gasification Combined Cycles (IGCC) and gas turbines work under conditions of high pressure, high temperature and flowing gas with high levels of CO2. The corrosion process occurring under such service conditions of modern power plants is different from that under current conditions with air combustion. The effect of pressure and chromium content on the corrosion reaction of steels at a constant temperature of 600°C (873K) is discussed in the present paper. The flowing gas is simulated as a mixture of 30% H2O und 70% CO2. The influence of chromium contents of 1, 2, 9 and 11% were experimentally observed.
Product tags
Also Purchased
Picture for 08446 High Temperature Oxidation of Heat-Resistant Alloys in Combustion Environments
Available for download

08446 High Temperature Oxidation of Heat-Resistant Alloys in Combustion Environments

Product Number: 51300-08446-SG
ISBN: 08446 2008 CP
Author: James Rakowski
Publication Date: 2008
$20.00
Picture for 08454 Stress Relaxation Cracking Of Welded Joints In Thick Sections Of Type-347 Stabilized Grade Of
Available for download

08454 Stress Relaxation Cracking Of Welded Joints In Thick Sections Of Type-347 Stabilized Grade Of Stainless Steel

Product Number: 51300-08454-SG
ISBN: 08454 2008 CP
Author: Christian E. van der Westhuizen
Publication Date: 2008
$20.00

This paper discusses reactors in hydrocarbon service that experienced numerous cracking problems over a 8-year period, where cracks were confined to the welded zones.  The material is  TP347 stainless steel, welded with E347-16 consumables.
Picture for 08462 SEM and Hot Corrosion Evaluation of 80Ni-20Cr Coating Applying Electrochemical Techniques
Available for download

08462 SEM and Hot Corrosion Evaluation of 80Ni-20Cr Coating Applying Electrochemical Techniques

Product Number: 51300-08462-SG
ISBN: 08462 2008 CP
Author: Cecilia Cuevas-Arteaga, Jesús Porcayo-Calderón, and Segio Serna
Publication Date: 2008
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support