08411 Hydrogen Production and Permeation of X-65 Pipeline Steel in Near Neutral pH Environments

Picture for 08411 Hydrogen Production and Permeation of X-65 Pipeline Steel in Near Neutral pH Environments
Available for download
Product Number: 51300-08411-SG
ISBN: 08411 2008 CP
Author: Stefanie Asher and Preet Singh
Publication Date: 2008
$0.00
$20.00
$20.00
Transgranular stress corrosion cracking (TGSCC) is a failure that occurs on buried carbon steel fuel transmission pipelines that are protectively coated and subjected to cathodic protection. Analysis of failed pipelines and previous research indicate that hydrogen is involved in the cracking process. However, the exact mechanism of crack initiation and hydrogen generation in near-neutral pH solutions was not clear. The objective of this research was to further understanding of the mechanism of TGSCC by determining the possible methods of hydrogen production and hydrogen diffusion into the pipeline steel. Specifically, this research focuses on the production of hydrogen through the interaction of iron with carbonic acid and bicarbonate. Hydrogen permeation testing and coupon exposure tests were used to understand the role of hydrogen in TGSCC. Effect of heat treatment and microstructure of X-65 pipeline steel of hydrogen diffusion was determined.
Transgranular stress corrosion cracking (TGSCC) is a failure that occurs on buried carbon steel fuel transmission pipelines that are protectively coated and subjected to cathodic protection. Analysis of failed pipelines and previous research indicate that hydrogen is involved in the cracking process. However, the exact mechanism of crack initiation and hydrogen generation in near-neutral pH solutions was not clear. The objective of this research was to further understanding of the mechanism of TGSCC by determining the possible methods of hydrogen production and hydrogen diffusion into the pipeline steel. Specifically, this research focuses on the production of hydrogen through the interaction of iron with carbonic acid and bicarbonate. Hydrogen permeation testing and coupon exposure tests were used to understand the role of hydrogen in TGSCC. Effect of heat treatment and microstructure of X-65 pipeline steel of hydrogen diffusion was determined.
Product tags
Also Purchased
Picture for 09120 - Hydrogen Effects on High Strength Pipeline Steels
Available for download

09120 Hydrogen Effects on High Strength Pipeline Steels

Product Number: 51300-09120-SG
ISBN: 09120 2009 CP
Author: Jeffrey Xie, Fraser King, Robert Yang
Publication Date: 2009
$20.00
Picture for 08405 Hydrogen Permeability Behavior of a High Strength Microalloyed Steel Developed for Sour Servic
Available for download

08405 Hydrogen Permeability Behavior of a High Strength Microalloyed Steel Developed for Sour Service

Product Number: 51300-08405-SG
ISBN: 08405 2008 CP
Author: S. Serna, B. Campillo, M. Ramirez, J. Gonzalez, I. Torres, and J. Juarez
Publication Date: 2008
$20.00
Picture for 08409 New Insights into Hydrogen Permeation in Steels: Measurements Through Thick Membranes
Available for download

08409 New Insights into Hydrogen Permeation in Steels: Measurements Through Thick Membranes

Product Number: 51300-08409-SG
ISBN: 08409 2008 CP
Author: Jean Kittel, Francois Ropital, and Julie Pellier
Publication Date: 2008
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support