07544 EFFECT OF AGEING ON THE CREEP-RUPTURE BEHAVIOR OF A GLASS-FIBER COMPOSITE EXPOSED TO AN AQUEOUS ENVIRONMENT

Picture for 07544 EFFECT OF AGEING ON THE CREEP-RUPTURE BEHAVIOR OF A GLASS-FIBER COMPOSITE EXPOSED TO AN AQUEOU
Available for download
Product Number: 51300-07544-SG
ISBN: 07544 2007 CP
Author: John Wolodko and Randy Petersen
Publication Date: 2007
$0.00
$20.00
$20.00
It is well-known that fiber reinforced composites made from glass-fibers are susceptible to both ageing effects and failure under constant loads (creep-rupture), particularly when exposed to water environments. There are very few experimental studies, however, which have dealt explicitly with the effect of exposure period (ageing) on the resulting creep-rupture response. Understanding this effect is particularly important when dealing with applications which are either delayed in entering full service or are being re-commissioned after some period of dormancy. In the current study, a preliminary examination is made to determine the influence of pre-conditioning period on the resulting time-to-failure curves for a glass-fiber reinforced epoxy system exposed to a water environment. Moisture absorption behavior and resulting failure characteristics are presented.
It is well-known that fiber reinforced composites made from glass-fibers are susceptible to both ageing effects and failure under constant loads (creep-rupture), particularly when exposed to water environments. There are very few experimental studies, however, which have dealt explicitly with the effect of exposure period (ageing) on the resulting creep-rupture response. Understanding this effect is particularly important when dealing with applications which are either delayed in entering full service or are being re-commissioned after some period of dormancy. In the current study, a preliminary examination is made to determine the influence of pre-conditioning period on the resulting time-to-failure curves for a glass-fiber reinforced epoxy system exposed to a water environment. Moisture absorption behavior and resulting failure characteristics are presented.
Product tags
Also Purchased
Picture for 09327 Corrosion Resistance of Various Glass Fiber Reinforcements
Available for download

09327 Corrosion Resistance of Various Glass Fiber Reinforcements

Product Number: 51300-09327-SG
ISBN: 09327 2009 CP
Author: Kevin Spoo
Publication Date: 2009
$20.00
Picture for 97359 QUALITY ASSURANCE OF GLASS FIBRE
Available for download

97359 QUALITY ASSURANCE OF GLASS FIBRE REINFORCED PIPING SYSTEMS

Product Number: 51300-97359-SG
ISBN: 97359 1997 CP
Author: C.A.M. van den Ende, J.C.M. de Bruijn
$20.00
Picture for 06038 Fiber Reinforced Crack Resistant
Available for download

06038 Fiber Reinforced Crack Resistant Epoxy Coatings

Product Number: 51300-06038-SG
ISBN: 06038 2006 CP
Author: Lars Thorslund Pedersen, Claus Kynding Jensen
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support