03532 HYDROGEN INDUCED CRACKING FAILURE OF SA 516 GRADE 70 STEEL IN NEAR NEUTRAL TO HIGH PH SOLUTION: PART 1 FIELD INVESTIGATION

Picture for 03532 HYDROGEN INDUCED CRACKING FAILURE OF
Available for download
Product Number: 51300-03532-SG
ISBN: 03532 2003 CP
Author: T.G. MARTIN, G. WILKEN
$0.00
$20.00
$20.00
During a major turn around at a sour gas treating facility, routine vessel entry revealed that a high- pressure amine contactor was apparently cracked. Follow up detailed ultrasonic inspection revealed severe cracking of the vessel, which was removed from service. A detailed failure investigation showed that the vessel had experienced severe hydrogen induced cracking ( HIC ), the cause of this cracking has been traced to high hydrogen fluxes brought on by a combination of operating conditions, poor metallurgy for the service and a tendency for the alkanolamine to charge hydrogen at very high acid gas Ioadings. Key Words: Hydrogen induced cracking, alkanolamines, sulfinoI-M, hydrogen permeation, sour service, pressure vessels
During a major turn around at a sour gas treating facility, routine vessel entry revealed that a high- pressure amine contactor was apparently cracked. Follow up detailed ultrasonic inspection revealed severe cracking of the vessel, which was removed from service. A detailed failure investigation showed that the vessel had experienced severe hydrogen induced cracking ( HIC ), the cause of this cracking has been traced to high hydrogen fluxes brought on by a combination of operating conditions, poor metallurgy for the service and a tendency for the alkanolamine to charge hydrogen at very high acid gas Ioadings. Key Words: Hydrogen induced cracking, alkanolamines, sulfinoI-M, hydrogen permeation, sour service, pressure vessels
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 03533 Hydrogen Induced Cracking Failure of ASTM
Available for download

03533 Hydrogen Induced Cracking Failure of ASTM A 516 Grade 70 Steel in Near Neutral to High pH Solution Part 2: Laboratory Studies

Product Number: 51300-03533-SG
ISBN: 03533 2003 CP
Author: T.G. Martin, G. Wilken
$20.00
Picture for Hydrogen Induced Cracking of A516 Plate Steels and the Apparent Effect of Microscopic Banding
Available for download

51316-7500-Hydrogen Induced Cracking of A516 Plate Steels and the Apparent Effect of Microscopic Banding

Product Number: 51316-7500-SG
ISBN: 7500 2016 CP
Author: Bryan Kulesza
Publication Date: 2016
$20.00
Picture for Effect of Microstructure on Hydrogen Induced Cracking and Sulfide Stress Cracking Property of Pressu
Available for download

51312-01204-Effect of Microstructure on Hydrogen Induced Cracking and Sulfide Stress Cracking Property of Pressu

Product Number: 51312-01204-SG
ISBN: 01204 2012 CP
Author: Sung Jin Kim
Publication Date: 2012
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support