Pitting and dealloying were observed when 70Ni/30Cu (UNS N04400) welded plates were exposed to artificial seawater containing sulfate-reducing bacteria. Attempts were made to differentiate biotic and abiotic corrosion mechanisms. Experiments were conducted in alternating aerobic/anaerobic conditions in the presence of inorganic sulfide and sulfate-reducing bacteria over the course of five months.
Keywords: Nickel-copper alloys, microbiologically influenced corrosion, weld, seawater, sulfate reducing bacteria, sulfide