01576 FAILURE ANALYSIS OF THE RING GEAR BEARING IN THE M198 HOWITZER

Picture for 01576 FAILURE ANALYSIS OF THE RING GEAR
Available for download
Product Number: 51300-01576-SG
ISBN: 01576 2001 CP
Author: Joseph Menke
$0.00
$20.00
$20.00
The traversing ring gear bearing assembly holds the upper and lower carriage assemblies of the howitzer together. When the ring gear bearing fractured, the gun tube fell to the ground. The failure analysis included destructive testing of the original gear and four additional gears to properly determine the cause of the fracture. Some fasteners holding the ring gear bearing assembly together failed due to hydrogen embrittlement but the cause of failure of the ring gear was stress corrosion cracking. Keywords: Stress-corrosion cracking, water intrusion, weapons system, hydrogen embrittlement, galvanic corrosion.
The traversing ring gear bearing assembly holds the upper and lower carriage assemblies of the howitzer together. When the ring gear bearing fractured, the gun tube fell to the ground. The failure analysis included destructive testing of the original gear and four additional gears to properly determine the cause of the fracture. Some fasteners holding the ring gear bearing assembly together failed due to hydrogen embrittlement but the cause of failure of the ring gear was stress corrosion cracking. Keywords: Stress-corrosion cracking, water intrusion, weapons system, hydrogen embrittlement, galvanic corrosion.
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 01573 CYCLIC POLARIZATION AND NON-DESTRUCTIVE
Available for download

01573 CYCLIC POLARIZATION AND NON-DESTRUCTIVE EVALUATION OF LASER INDUCED SURFACE IMPROVEMENT (LISI) ON STEEL AND ALUMINUM SUBSTRATES

Product Number: 51300-01573-SG
ISBN: 01573 2001 CP
Author: NORRIS LINDSEY AND K.L. VASANTH
$20.00
Picture for 01581 ORIGIN AND VALIDATION OF THE 100 mV
Available for download

01581 ORIGIN AND VALIDATION OF THE 100 mV POLARIZATION CRITERION

Product Number: 51300-01581-SG
ISBN: 01581 2001 CP
Author: Thomas J. Barlo
$20.00
Picture for 01557 Fundamental Investigation on the Kinetics
Available for download

01557 Fundamental Investigation on the Kinetics of the Rust Removal by Hydroxyethane Diphosphonic Acid (HEDPA).

Product Number: 51300-01557-SG
ISBN: 01557 2001 CP
Author: A. Srinivasa Rao
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support