00182 COMPARISON OF THE CREVICE CORROSION RESISTANCE OF ALLOYS 625 AND 22 IN CONCENTRATED CHLORIDE SOLUTION FROM 60 TO 95°C

Picture for 00182 COMPARISON OF THE CREVICE CORROSION
Available for download
Product Number: 51300-00182-SG
ISBN: 00182 2000 CP
Author: B.A. Kehler, G.O. Ilevbare, J.R. Scully
$0.00
$20.00
$20.00
The effects of electrolyte composition and oxide film age on the crevice corrosion properties of alloys 625 and 22 were studied at temperatures ranging from 60 to 95oC in concentrated chloride electrolytes. Critical potentials were determined using conventional current density thresholds and comparisons were made between alloys 625 and 22 on the basis of these critical potentials. Air aged alloy 22 specimens exhibited the highest resistance to crevice corrosion at 95°C in terms of critical crevice potentials, while freshly polished alloy 22 exhibited the lowest resistance. Studies over the entire temperature range showed that air aged alloy 22 is more resistant to crevice corrosion than air aged alloy 625 as evidenced by higher critical crevice potentials. As the temperature was lowered from 95 to 80°C, critical crevice potentials for alloy 22 either approached or exceeded experimentally determined Cr (Mo, Ni) transpassive potentials. Key Words: alloy 625, alloy 22, nuclear waste containment, crevice corrosion, chloride, critical crevice potential, repassivation potential, cyclic potentiodynamic polarization
The effects of electrolyte composition and oxide film age on the crevice corrosion properties of alloys 625 and 22 were studied at temperatures ranging from 60 to 95oC in concentrated chloride electrolytes. Critical potentials were determined using conventional current density thresholds and comparisons were made between alloys 625 and 22 on the basis of these critical potentials. Air aged alloy 22 specimens exhibited the highest resistance to crevice corrosion at 95°C in terms of critical crevice potentials, while freshly polished alloy 22 exhibited the lowest resistance. Studies over the entire temperature range showed that air aged alloy 22 is more resistant to crevice corrosion than air aged alloy 625 as evidenced by higher critical crevice potentials. As the temperature was lowered from 95 to 80°C, critical crevice potentials for alloy 22 either approached or exceeded experimentally determined Cr (Mo, Ni) transpassive potentials. Key Words: alloy 625, alloy 22, nuclear waste containment, crevice corrosion, chloride, critical crevice potential, repassivation potential, cyclic potentiodynamic polarization
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 00181 INFLUENCE OF AGING ON MICROSTRUCTURE
Available for download

00181 INFLUENCE OF AGING ON MICROSTRUCTURE, MECHANICAL PROPERTIES, AND CORROSION RESISTANCE OF A Ni-22Cr-13Mo-3W ALLOY.

Product Number: 51300-00181-SG
ISBN: 00181 2000 CP
Author: Rau1 B. Rebak, Natalie E. Koon, Jeffrey R. Dillman and Paul Crook, Tammy S. E. Summers
$20.00
Picture for 00186 STRAIN AND MICROSTRUCTURE CHARACTERIZATION
Available for download

00186 STRAIN AND MICROSTRUCTURE CHARACTERIZATION OF AUSTENITIC STAINLESS STEEL WELD HAZS

Product Number: 51300-00186-SG
ISBN: 00186 2000 CP
Author: T.M. Angeliu, P.L. Andresen, E. Hall, J.A. Sutliff, S. Sitzman
$20.00
Picture for 00185 CHARACTERIZING THE CREEP BEHAVIOR OF
Available for download

00185 CHARACTERIZING THE CREEP BEHAVIOR OF AUSTENITIC ALLOYS RELEVANT TO THE CRACK TIP STRAIN RATE AND BWR SCC

Product Number: 51300-00185-SG
ISBN: 00185 2000 CP
Author: Thomas M. Angeliu
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support