Preventing Corrosion under Insulation in Piping - Trends after Evaluating Digital Data from Thousands of Piping Circuits

Product Number: 51323-18871-SG

Author: Eddie Sanchez, Michael Townsend, Michael Nichols, Katherine Jonsson, Eric Sjerve, Ana Benz

Publication Date: 2023

$20.00

Extensive guidelines have been published for selecting where to search for corrosion under insulation (CUI). The guidelines are based on CUI failures and near misses. Piping CUI inspection programs collect the data outlined as relevant in specific company practices.

Available for download

Proactive Cleaning, Maintenance and Inspection of Vessel Hulls Via Autonomous Robots

Product Number: 51323-19315-SG

Author: Karl Lander

Publication Date: 2023

$20.00

Prevention of corrosion on submerged surfaces, particularly ship’s hulls, is a challenging process. Beyond the corrosive effects of seawater, biofouling will start to accumulate, and if left unchecked, can potentially damage the coating reducing its anti-corrosive properties. In stationery applications, the biofouling may be of little immediate significance, but in the case of vessels, biofouling will greatly increase hull resistance, leading to reduced speed, greater fuel consumption and emissions, as well as enabling the transfer of alien species as the vessels travel the globe.

Available for download

Proposal of a New Corrosion Index for Domestic Tap Water In Japan

Product Number: 51323-19056-SG

Author: Yuji Nakamura, Yasuki Matsukawa, Shinji Okazaki, Shukuji Asakura

Publication Date: 2023

$20.00

Japanese tap water has a low calcium hardness compared with those of countries in Europe and the Americas. There are many steep mountains and volcanos in Japan. These geological factors lead to features such as short rivers with water rich in SiO2. This leads to a lack of calcium compounds in river water because the flow rate is high and the dissolution rate of CaCO3 into water is low.

Available for download

Protective Coatings Against Formation of Scale Deposits

Product Number: 51323-19528-SG

Author: P.D. Natsi, E. Zande, P.G. Koutsoukos

Publication Date: 2023

$20.00

Polymers have played an essential role in development of technology, applied engineering, and materials. Metallic counterparts in medical, construction, energy, water treatment, and electronic applications, are often replaced by polymers. Their characteristics such as wide range of elasticity, strength and degradability make them ideal for numerous applications.

Available for download

Qualification of Low Temperature Cure, Thin-Film Linings for Aboveground Storage Tanks

Product Number: 51323-18767-SG

Author: Haralampos Tsaprailis, Shan Rao, Jiajun Liang

Publication Date: 2023

$20.00

This paper presents the laboratory qualification program utilized to compare four lining systems for application down to -10°C (14°F). The lining systems were applied and cured at -10 °C (14 °F). Cure of the lining systems was monitored using differential scanning calorimetry and adhesion testing, while the performance of the linings was evaluated using electrochemical impedance spectroscopy, and autoclave and standard atlas cell testing. One of the four lining systems, Product C, a 71% volume solids epoxy that contained zinc phosphate, exhibited the most potential for low temperature field implementation.

Available for download

Quantifying High Temperature Corrosion in Renewable Diesel and Sustainable Aviation Fuel Production

Product Number: 51323-19457-SG

Author: Sridhar Srinivasan, Winston Robbins, Gerrit Buchheim

Publication Date: 2023

$20.00

In Corrosion/2021, the authors introduced a molecular mechanistic model that quantifies and predicts simultaneous naphthenic acid and sulfidation (SNAPS) corrosion rates. During Corrosion/2022, we presented the mechanistic corrosion prediction framework describing the molecular basis of the model’s reactions, kinetics, and mass transport of reactive organic sulfur compounds (ROSC) to vessel walls. In this molecular model, sulfidation corrosion is calculated for direct heterolytic reaction of ROSC with solid surfaces.

Available for download

Raman and FT-IR Based Methodology Development to Assess Flexible Pipelines Pressure Barrier Degradation in Offshore Installations of the Oil and Gas Industry

Product Number: 51323-18997-SG

Author: Elaine F. Silva, Luciene S. Santos, Merlin C. E. Bandeira, Oscar R. Mattos, Nara Guidacci Berry, Sylvia C. S. Teixeira, Antonio H.M.F.T Silva, Erica G. Chaves

Publication Date: 2023

$20.00

During operation, due to offshore production environment exposure, the sealing barrier of the flexible pipes can be damaged because of polymer chains degradation. There is great interest in understanding the influence of pressure, temperature, fluid composition, and supercritical CO2 on degradation of flexible pipes sealing barrier materials. Therefore, it is extremely relevant a qualitative study of deleterious effects of each one of the factors mentioned above.

Available for download

Reactive to Proactive Transformation - A New Paradigm in Corrosion Management

Product Number: 51323-19106-SG

Author: Faisal M. Al-Mutahhar, Ibrahim A. Albrahim, Abdullah M. Alratoee, Rakan A. Al-Shebil, Ayman A. Alabdullatif, Ricardo S. Costa, Yousef A. Aldossary, Muntathir M. Al-Jumaah

Publication Date: 2023

$20.00

Maximizing asset uptime and reducing maintenance costs are essential in any process facility. Effective corrosion management is a key driver to achieving these goals. Corrosion management involves monitoring and controlling corrosion to maintain the integrity of equipment and improve availability and safety.

Available for download

Real Time Sour Water Corrosion Prediction for Fluid Catalytic Cracking Overhead System

Product Number: 51323-18785-SG

Author: H. Li, P. Constantineau, C. Zhuang, Y. H. Hou

Publication Date: 2023

$20.00

Crude feed often contains contaminants / heavy amounts of sulfur compounds that may degrade equipment or even the finished product. These sulfur and nitrogen compounds react with hydrogen to form hydrogen sulfide (H2S) and ammonia (NH3) within certain units and can lead to formation of ammonium bisulfide salts (NH4HS) when cooled. NH4HS salts may lead to plugging, and if wet, rapid under deposit corrosion can occur. Hence, water washing ahead of NH4HS salt formation is essential to prevent wet salt corrosion and ensure safe unit operations.

Available for download

Real-time measurement of organic coating performance for atmospheric galvanic corrosion protection

Product Number: 51323-19036-SG

Author: Victoria Avance, Lindsay Davis, Brandi Clark, Fritz Friedersdorf

Publication Date: 2023

$20.00

The corrosion of aircraft costs the U.S. Department of Defense more than $20 billion annually and accounts for approximately 20% of all maintenance. Coatings are the most effective way to protect aircraft, but they have a finite lifetime and must be maintained or replaced before the underlying substrate is damaged by corrosion. Current aircraft maintenance practices call for coating inspections and repairs based on elapsed time and not on measurements of coating health.

Available for download

Recent Advancements of Corrosion Inhibitors Using Graphene Oxide-Based Nanomaterial

Product Number: 51323-19268-SG

Author: Bader Alharbi, Norah Aljeaban, Ahmed Busaleh, Tawfik A. Saleh

Publication Date: 2023

$20.00

The corrosion is a spontaneous chemical reaction connected to heat exchangers and pipelines that degrades the strength and quality of utilized steel. The aggressive environment, which is ongoing, intense, and frequently difficult to totally prevent, is the key factor contributing to the metal's deterioration. Additionally, it demonstrates a serious economic problem that causes industrial operational assets to require expensive repairs, ruining the public space.

Available for download

Redefining Corrosion Resistance Requirements for Austenitic Stainless Steels used in Drilling Applications – Part 2: CrNi-Stainless Steels

Product Number: 51323-19277-SG

Author: Julia Ditmann, Helmuth Sarmiento Klapper, Thomas Williams, Bernd Holper, Krutibas Panda, Reece Goldsberry, Wendy Martin, Daryl McIntyre, Clara Herrera, Merlin Seifert

Publication Date: 2023

$20.00

Pitting and environmentally assisted cracking (EAC) are a major concern when austenitic CrMn-stainless steels, which are commonly used for non-magnetic drill collars (NMCD), are exposed to high halide-containing drilling fluids. Even though the fast propagation of environmentally assisted cracks can partially be controlled by the introduction of compressive residual stresses, surface treatments are not intended to address localized corrosion resistance. In fact, it has been demonstrated that CrMn-stainless steels become prone to pitting corrosion when exposed to high Cl- streams at elevated temperature, which ultimately can also lead to stress corrosion cracking (SCC) when sufficient stresses are present.

Products tagged with 'ampp annual conference + expo 2023'

Association for Materials Protection and Performance