This paper presents work in follow-up to the previous study. It is focused on UNS1 N07718, UNS N09925, UNS N07725 and UNS N09946. A series of incremental step load tests of compact tensile specimens were conducted to measure the fracture toughness during testing and cracking was monitored by the Electric Crack Growth Monitoring technique. A new engineering technique, referred to as statistical fractography, was used to investigate the fracture surface morphology and extract from it the fracture properties of the alloys.
We are unable to complete this action. Please try again at a later time.
If this error continues to occur, please contact AMPP Customer Support for assistance.
Error Message:
Please login to use Standards Credits*
* AMPP Members receive Standards Credits in order to redeem eligible Standards and Reports in the Store
You are not a Member.
AMPP Members enjoy many benefits, including Standards Credits which can be used to redeem eligible Standards and Reports in the Store.
You can visit the Membership Page to learn about the benefits of membership.
You have previously purchased this item.
Go to Downloadable Products in your AMPP Store profile to find this item.
You do not have sufficient Standards Credits to claim this item.
Click on 'ADD TO CART' to purchase this item.
Your Standards Credit(s)
1
Remaining Credits
0
Please review your transaction.
Click on 'REDEEM' to use your Standards Credits to claim this item.
You have successfully redeemed:
Go to Downloadable Products in your AMPP Store Profile to find and download this item.
A cold-worked carbon steel pulsation dampener located on a glycol circulation pump failed catastrophically in service. The two parts of the failed dampener were projected several tens of meters across the offshore facility. The failure was investigated initially using traditional metallurgical techniques, but this failed to reach a conclusive failure mechanism.