In ship's ballast tanks, most of coating failures (and corrosion attacks) were observed on sharp steel edges, welds seams and weld spatters. One solution is to employ high solid coating material with less tendency to flow away from edges. In this study, two coatings are selected and evaluated in terms of their edge retention ability.
We are unable to complete this action. Please try again at a later time.
If this error continues to occur, please contact AMPP Customer Support for assistance.
Error Message:
Please login to use Standards Credits*
* AMPP Members receive Standards Credits in order to redeem eligible Standards and Reports in the Store
You are not a Member.
AMPP Members enjoy many benefits, including Standards Credits which can be used to redeem eligible Standards and Reports in the Store.
You can visit the Membership Page to learn about the benefits of membership.
You have previously purchased this item.
Go to Downloadable Products in your AMPP Store profile to find this item.
You do not have sufficient Standards Credits to claim this item.
Click on 'ADD TO CART' to purchase this item.
Your Standards Credit(s)
1
Remaining Credits
0
Please review your transaction.
Click on 'REDEEM' to use your Standards Credits to claim this item.
You have successfully redeemed:
Go to Downloadable Products in your AMPP Store Profile to find and download this item.
Stress development in epoxy coatings applied in water ballast tanks (WBT) on ships can lead to cracking, corrosion, and failure of ship’s hulls, with catastrophic consequences to the environment as well as loss of seamen at sea. Typically, these cracks do not appear during application and curing of the coating but after some finite time of service. The financial wellbeing of the ship’s owner can suffer greatly. To avoid such cracking, it is critical to have a clear understanding of the underlying mechanisms and primary controlling factors behind the coating cracks.