Nickel alloys UNS N06625, UNS N06059, UNS N06022, UNS N08825 and one Special Stainless Steel (UNS N08031) are overlay welded in 1 to 3 layers on carbon steel. The dilution is measured and results of pitting corrosion in an immersion test with “Green Death” solution will be discussed.
We are unable to complete this action. Please try again at a later time.
If this error continues to occur, please contact AMPP Customer Support for assistance.
Error Message:
Please login to use Standards Credits*
* AMPP Members receive Standards Credits in order to redeem eligible Standards and Reports in the Store
You are not a Member.
AMPP Members enjoy many benefits, including Standards Credits which can be used to redeem eligible Standards and Reports in the Store.
You can visit the Membership Page to learn about the benefits of membership.
You have previously purchased this item.
Go to Downloadable Products in your AMPP Store profile to find this item.
You do not have sufficient Standards Credits to claim this item.
Click on 'ADD TO CART' to purchase this item.
Your Standards Credit(s)
1
Remaining Credits
0
Please review your transaction.
Click on 'REDEEM' to use your Standards Credits to claim this item.
You have successfully redeemed:
Go to Downloadable Products in your AMPP Store Profile to find and download this item.
An operator in North America discovered an internal corrosion failure in a wet gas system directly below the point of injection of a water-soluble corrosion inhibitor (CI). Tests using low shear rotating cage autoclaves and a dual autoclave system were performed as a corrosion screening method.
Several components in geothermal power plants need to be protected from the environment due to the corrosive nature of geothermal fluids used to generate the energy. Depending on the fluid properties for any location, the type of protection varies. In geothermal power plants, wear, erosion, corrosion, and scaling are all known problems1. These issues can lead to a variety of outcomes, ranging from decreased plant efficiency to upstream component failure. Failure of a component is thus a significant challenge in the geothermal industry, where materials need to operate in high temperature and high pressure environments. A major cost factor is also linked to the drilling of geothermal wells, where cost rises due to increased depth/distance of drilling, increased trip times, higher high temperature and high-pressure conditions which can lead to increased wear and corrosion of the materials. To address the issue, coatings can be considered to be a potential solution to extend the service life of downhole equipment.
This study focuses on a better understanding of pitting and crevice corrosion on coating surface damaged carbon steels in automotive applications. Immersion and cyclic polarization tests were conducted on bare and coated metals in a 5% NaCl solution.