Aircraft representative galvanic test articles and witness coupons were placed out for atmospheric exposure testing at the U.S. Naval Research Lab (NRL) site in Key West, Florida. One set of test specimens was exposed to only ambient environment for a 62 day period; a second set of test specimens was exposed to both ambient environment (initial 62 days), and a short duration, twice daily, seawater spray protocol over a further 55 day period. Environmental loading was monitored using sensors that measured temperature, relative humidity, rainfall, and time of wetness (TOW), at 30 minute intervals. Following retrieval, the test articles were inspected in the laboratory using laser profilometry to characterize the spatial distribution and depth of corrosion damage. Mass loss measurement using the witness coupons was used to estimate relative corrosion rates for the two periods.