Microstructural characterization and Corrosion-wear properties of Graphene oxide/ Polytetrafluoroethylene Coatings for Geothermal Drilling Applications

Product Number: 51321-16474-SG
Author: Gifty Oppong Boakye/Danyil Kovalov/Erlend Oddvin Straume/Beatrice Alonso Rodriguez/Danyil Kovalov/Sigrun Nanna Karlsdottir
Publication Date: 2021
$0.00
$20.00
$20.00

Polymeric coatings are exploited by adding reinforcements to maximize its industrial performance. The idea of reinforcement is to tailor the matrix's wide-range performance to a specific desired property to prevent component failures. In this work, the polyphenylene sulfide-polytetrafluoroethylene (PPS-PTFE) matrix was modified with graphene oxide (GO) to improve the mechanical properties, corrosion and wear resistance, to provide coatings for drilling components for high-temperature geothermal well environment. Electrochemical test in a 3.5wt% NaCl solution and a pin-on-disc sliding test were performed to determine the corrosion and wear resistance of the novel coatings. The addition of GO reduced the coefficient of friction but increased the roughness and hydrophobic properties of the coatings. The tendency of coatings to minimize corrosion were determined by evaluating the open circuit potential (OCP), corrosion potential (Ecorr) and corrosion current density (Icorr). The coatings showed higher OCP, Ecorr and lower Icorr after 24 hours of immersion. The 1wt% GO polymer coating is the most promising; based on the reduction of Icorr of the substrate from 0.15 µA to 0.01 µA and an increased friction and wear resistance by approximately 72%. The results indicate a good coating performance for low GO reinforcement by improvement in surface properties, corrosion and wear resistance.

Keywords: abrasive wear, corrosion, graphene oxide, geothermal, Geo-Drill, hydrophobicity, PPSPTFE/GO coating.

Polymeric coatings are exploited by adding reinforcements to maximize its industrial performance. The idea of reinforcement is to tailor the matrix's wide-range performance to a specific desired property to prevent component failures. In this work, the polyphenylene sulfide-polytetrafluoroethylene (PPS-PTFE) matrix was modified with graphene oxide (GO) to improve the mechanical properties, corrosion and wear resistance, to provide coatings for drilling components for high-temperature geothermal well environment. Electrochemical test in a 3.5wt% NaCl solution and a pin-on-disc sliding test were performed to determine the corrosion and wear resistance of the novel coatings. The addition of GO reduced the coefficient of friction but increased the roughness and hydrophobic properties of the coatings. The tendency of coatings to minimize corrosion were determined by evaluating the open circuit potential (OCP), corrosion potential (Ecorr) and corrosion current density (Icorr). The coatings showed higher OCP, Ecorr and lower Icorr after 24 hours of immersion. The 1wt% GO polymer coating is the most promising; based on the reduction of Icorr of the substrate from 0.15 µA to 0.01 µA and an increased friction and wear resistance by approximately 72%. The results indicate a good coating performance for low GO reinforcement by improvement in surface properties, corrosion and wear resistance.

Keywords: abrasive wear, corrosion, graphene oxide, geothermal, Geo-Drill, hydrophobicity, PPSPTFE/GO coating.

Also Purchased
Picture for 00700 FAILURE OF POLYPROPYLENE LINED PIPE IN
Available for download

00700 FAILURE OF POLYPROPYLENE LINED PIPE IN SULFURIC ACID - A CASE HISTORY

Product Number: 51300-00700-SG
ISBN: 00700 2000 CP
Author: Ali A. A1-Beed
$20.00
Picture for 00551 CORROSION BARRIER DETERIORATION AND
Available for download

00551 CORROSION BARRIER DETERIORATION AND DETECTION IN FRP STRUCTURES

Product Number: 51300-00551-SG
ISBN: 00551 2000 CP
Author: Paul A. Sprague, P.E., Hira S. Ahluwalia
$20.00
Picture for 00322 SCALE CONTROL IN GEOTHERMAL
Available for download

00322 SCALE CONTROL IN GEOTHERMAL SYSTEMS

Product Number: 51300-00322-SG
ISBN: 00322 2000 CP
Author: Libardo A. Perez
$20.00