51318-11472-Investigation of the Lower Threshold Value of pH2S for Retardation of CO2 Pitting Attack

Picture for Investigation of the Lower Threshold Value of pH2S for Retardation of CO2 Pitting Attack
Available for download

A series of experiments was conducted in a large-scale multi-phase flow loop to investigate the threshold level of H2S leading to localized attack on mild steel in CO2 saturated aqueous solution with 1%wt NaCl at 40°C.

Product Number: 51318-11472-SG
Author: Wei Yan / Bruce Brown / Srdjan Nesic
Publication Date: 2018
Industry: Science of Corrosion
$0.00
$20.00
$20.00

A series of experiments was conducted in a large-scale multi-phase flow loop to investigate the threshold level of H2S leading to localized attack on mild steel in CO2 saturated aqueous solution with 1%wt NaCl at 40°C.The CO2 partial pressure was fixed at 8.0 bar in all test conditions and the H2S partial pressure was varied from 0.024mbar (3ppm) to 0.5mbar (60 ppm). The superficial liquid velocity was 0.8 m/s and the experiment duration was between 2 and 21 days. The experimental results revealed that when the H2S partial pressure was low and the saturation value for mackinawite was near unity, localized attack occurred. Using the methodology provided, the corrosion behavior in very low pH2S environments may be predicted according to the super saturation levels of mackinawite.

 

Keywords: low H2S corrosion; localized attack; threshold value; mild steel

A series of experiments was conducted in a large-scale multi-phase flow loop to investigate the threshold level of H2S leading to localized attack on mild steel in CO2 saturated aqueous solution with 1%wt NaCl at 40°C.The CO2 partial pressure was fixed at 8.0 bar in all test conditions and the H2S partial pressure was varied from 0.024mbar (3ppm) to 0.5mbar (60 ppm). The superficial liquid velocity was 0.8 m/s and the experiment duration was between 2 and 21 days. The experimental results revealed that when the H2S partial pressure was low and the saturation value for mackinawite was near unity, localized attack occurred. Using the methodology provided, the corrosion behavior in very low pH2S environments may be predicted according to the super saturation levels of mackinawite.

 

Keywords: low H2S corrosion; localized attack; threshold value; mild steel

Product tags
Also Purchased
Picture for Corrosion evaluation of tubing steels and material selection in the CO2/H2S coexistent environme
Available for download

51318-11477-Corrosion evaluation of tubing steels and material selection in the CO2/H2S coexistent environment

Product Number: 51318-11477-SG
Author: Nai-yan ZHANG / Zhi ZHANG / Wen-tao ZHAO / Lian LIU / Taihe SHI
Publication Date: 2018
$20.00

To evaluate the applicability of the tubing steels, the corrosion behavior and stress corrosion cracking of tubing steels (P110S, P110-13Cr and duplex stainless steel 2205) were investigated under different H2S partial pressures and temperature.
Picture for EVALUATION OF THE STRESS CORROSION CRACKING OF DIFFERENT CRAS IN SOUR WELL ENVIRONMENT.
Available for download

51318-11450-EVALUATION OF THE STRESS CORROSION CRACKING OF DIFFERENT CRAS IN SOUR WELL ENVIRONMENT.

Product Number: 51318-11450-SG
Author: P.Esteban / Alejandra López / B.Calleja
Publication Date: 2018
$20.00

This paper shows the results of the stress corrosion cracking evaluation of two different austenitic corrosion resistant alloys (CRAs), N08028 and N08825 under different conditions of temperature and pressure of H2S and CO2.
Picture for Investigation of the applicability of droplet transport for TLC mitigation
Available for download

51318-11493-Investigation of the applicability of droplet transport for TLC mitigation

Product Number: 51318-11493-SG
Author: Nicolas Jauseau / Fernando Farelas / Marc Singer / Srdjan Nesic
Publication Date: 2018
$20.00

This work presents a combined modeling and experimental methodology to determine the onset of droplet entrainment from the bottom and deposition at the top of the line.

 
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support