51314-3891-Improvement of Corrosion Resistance of Sheet Piling in Sea Water

Product Number: 51314-3891-SG
ISBN: 3891 2014 CP
Author: Christoph Bosch
Publication Date: 2014
$0.00
$20.00
$20.00
Development of structural steels with improved corrosion resistance is gaining significance for use in offshore structures. Corrosion of structural steel depends on various influencing factors such as location of seaport or seawater corrosivity zone the steel is exposed in but also on the chemical composition of the steel itself.Against this background the influence of alloying additions of copper chromium and nickel which to the state of knowledge are able to mitigate corrosion by seawater was investigated aiming at an economic alloy modification of structural steels used for manufacture of sheet piling.Laboratory corrosion tests were conducted with the rotating cage test setup. As a reference the corrosion performance of standard structural steel grades in the strength range of 275 MPa to 500 MPa was determined. The influence of alloying additions of copper chromium and nickel was investigated in further test series using industrially manufactured sheet piling including a steel manufactured in accordance with ASTM A 690.From the investigated alloy variants the steels alloyed with about 0.3 % copper are particularly suitable for reduction of general corrosion in sea water up to 40 %. In order to ensure the workability of copper alloyed components usually an adequate amount of Ni is added. As the corrosion test results e.g. for the copper/nickel alloyed steel ASTM A 690 show such a measure is not recommended if improved corrosion resistance in sea water is envisaged. 
Development of structural steels with improved corrosion resistance is gaining significance for use in offshore structures. Corrosion of structural steel depends on various influencing factors such as location of seaport or seawater corrosivity zone the steel is exposed in but also on the chemical composition of the steel itself.Against this background the influence of alloying additions of copper chromium and nickel which to the state of knowledge are able to mitigate corrosion by seawater was investigated aiming at an economic alloy modification of structural steels used for manufacture of sheet piling.Laboratory corrosion tests were conducted with the rotating cage test setup. As a reference the corrosion performance of standard structural steel grades in the strength range of 275 MPa to 500 MPa was determined. The influence of alloying additions of copper chromium and nickel was investigated in further test series using industrially manufactured sheet piling including a steel manufactured in accordance with ASTM A 690.From the investigated alloy variants the steels alloyed with about 0.3 % copper are particularly suitable for reduction of general corrosion in sea water up to 40 %. In order to ensure the workability of copper alloyed components usually an adequate amount of Ni is added. As the corrosion test results e.g. for the copper/nickel alloyed steel ASTM A 690 show such a measure is not recommended if improved corrosion resistance in sea water is envisaged. 
Product tags
Also Purchased
Picture for 10393 Diagnosis, Numerical Modeling and Devlopment of the Cathodic Protection Refurbishing
Available for download

10393 Diagnosis, Numerical Modeling and Devlopment of the Cathodic Protection Refurbishing of the Metal Sheet Piling of the Docks of Quetzal Marine Terminal in Guatemala

Product Number: 51300-10393-SG
ISBN: 10393 2010 CP
Author: L Martinez de la Escalera, O Alvarez, J Canto, H Rivera, A Godoy, H Ventura, J Ascencio, L Martinez
Publication Date: 2010
$20.00
Picture for 05224 Factors Affecting Corrosion Performance and
Available for download

05224 Factors Affecting Corrosion Performance and Testing of Materials and Components in Sea Water

Product Number: 51300-05224-SG
ISBN: 05224 2005 CP
Author: David A. Shifler and Denise M. Aylor, Naval Surface Warfare Center
$20.00
Picture for Minimizing the Grounding Resistance of Compact Cathodic Protection Anodic Beds with Finite Element M
Available for download

51314-3859-Minimizing the Grounding Resistance of Compact Cathodic Protection Anodic Beds with Finite Element Method

Product Number: 51314-3859-SG
ISBN: 3859 2014 CP
Author: Chengwei Xu
Publication Date: 2014
$20.00