51318-11405-Erosion-corrosion evaluation of two white cast irons under severe conditions in oil sands industry

  • /
  • 51318-11405-Erosion-corrosion evaluation of two white cast irons under severe conditions in oil sands industry
Picture for Erosion-corrosion evaluation of two white cast irons under severe conditions in oil sands industry
Available for download

In the current study, two white cast irons were evaluated under severe conditions; a 27% Cr alloy (27WCI) with eutectic chromium carbides and another 30% Cr alloy (30WCI) with primary chromium carbides and higher carbide volume fraction than the 27WCI

Product Number: 51318-11405-SG
Author: George Karafyllias / Edward Humphries / Alexander Galloway
Publication Date: 2018
$0.00
$20.00
$20.00

In the oil sands industry, the erosion-corrosion phenomena are enhanced due to the presence of abrasive solid particles. Thus, in order to prevent failures in engineering components such as pumps and pipelines, corrosion and mainly erosion resistant materials are selected. The white cast irons comprise an attractive candidate for these applications since their hard metallic matrix and chromium carbides can mitigate the erosive attack. However, due to their brittleness and complex microstructure, a careful material selection strategy must be conducted with respect to the operational conditions and, in particular, the size of the erodent particles. In the current study, two white cast irons were evaluated under severe conditions; a 27% Cr alloy (27WCI) with eutectic chromium carbides and another 30% Cr alloy (30WCI) with primary chromium carbides and higher carbide volume fraction than the 27WCI. The evaluation was performed using a submerged jet apparatus in fresh water containing angular silica sand particles with 500 μm diameter on average. Also, the application of cathodic protection contributed to understand the interactions between erosion and corrosion related mechanisms. The most prominent finding was the superiority of the 27WCI alloy over the 30WCI, which was linked to the brittleness of primary carbides and the size of erodent particles.

Key words: Erosion-corrosion, cast irons, impingement, chromium carbides, cathodic protection

 

 

In the oil sands industry, the erosion-corrosion phenomena are enhanced due to the presence of abrasive solid particles. Thus, in order to prevent failures in engineering components such as pumps and pipelines, corrosion and mainly erosion resistant materials are selected. The white cast irons comprise an attractive candidate for these applications since their hard metallic matrix and chromium carbides can mitigate the erosive attack. However, due to their brittleness and complex microstructure, a careful material selection strategy must be conducted with respect to the operational conditions and, in particular, the size of the erodent particles. In the current study, two white cast irons were evaluated under severe conditions; a 27% Cr alloy (27WCI) with eutectic chromium carbides and another 30% Cr alloy (30WCI) with primary chromium carbides and higher carbide volume fraction than the 27WCI. The evaluation was performed using a submerged jet apparatus in fresh water containing angular silica sand particles with 500 μm diameter on average. Also, the application of cathodic protection contributed to understand the interactions between erosion and corrosion related mechanisms. The most prominent finding was the superiority of the 27WCI alloy over the 30WCI, which was linked to the brittleness of primary carbides and the size of erodent particles.

Key words: Erosion-corrosion, cast irons, impingement, chromium carbides, cathodic protection

 

 

Product tags
Also Purchased
Picture for Novel Ni-B/AlN nanocomposite coatings for oil and gas industry
Available for download

51318-11399-Novel Ni-B/AlN nanocomposite coatings for oil and gas industry

Product Number: 51318-11399-SG
Author: Bahgat Radwan / Said Elmi Ahmed / Ramazan Kahraman / F.M. Montemor / Kamran Ali / Abdelrahman Adel Mahmoud / R. A. Shakoor
Publication Date: 2018
$20.00

Ni–B/AlN (nickel-boron / aluminum nitride) nanocomposite coatings were synthesized through electrodeposition technique and their properties were investigated.

 
Picture for New Sacrificial Anodic Alloys
Available for download

51318-11388-New Sacrificial Anodic Alloys

Product Number: 51318-11388-SG
Author: Vladimir Kechin / Efim Lyublinski
Publication Date: 2018
$20.00

Alloys test results establish the relationship between electrochemical, chemical & metallurgical properties of magnesium, aluminum and zinc alloys and achieve higher and more stable current consumption of sacrificial anodes.
Picture for Ni-Co Electroplating as Corrosion Protection for Carbon Steel Fasteners used in Oil and Gas
Available for download

51318-11391-Ni-Co Electroplating as Corrosion Protection for Carbon Steel Fasteners used in Oil and Gas

Product Number: 51318-11391-SG
Author: Omar Rosas / Jose Hernandez / Oscar Garcia / Carlos Girault
Publication Date: 2018
$20.00

In the present work, the corrosion resistance of carbon steel studs coated with Ni-Co, Cd, Zn, and Zn-Ni was tested and measured by electrochemical techniques and environmental exposure tests.
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support