51318-11535-Comparison of Slow Strain Rate Incremental Step Load and Rising Displacement Hydrogen Embrittlement Testing of UNS N07718

The influence of loading mode and specimen geometry on the measured hydrogen embrittlement susceptibility of UNS N07718 (alloy 718) has been assessed.

Product Number: 51318-11535-SG
Author: Brian Kagay / Kip Findley / Steve Coryell
Publication Date: 2018
$0.00
$20.00
$20.00

The influence of loading mode and specimen geometry on the measured hydrogen embrittlement susceptibility of UNS N07718 (alloy 718) has been assessed. Slow strain rate (SSR) experiments were performed with smooth specimens, while incremental step load (ISL) testing and rising displacement (RD) testing were performed on circular notch tensile (CNT) specimens with cathodic hydrogen charging. Several microstructures of alloy 718 with different strength levels and amounts of grain boundary δ phase precipitation were evaluated. Fracture modes were also evaluated with scanning electron microscopy and correlated to the microstructures and testing methods. Hydrogen embrittlement susceptibilities and fracture modes were similar for each test method and were highly dependent on microstructure. It is interpreted that hydrogen-affected cracking of alloy 718 requires a certain level of plasticity and an adequate amount of absorbed hydrogen in both the SSR test and the accelerated fracture mechanics ISL and RD tests. These criteria are related to the measured threshold stress intensity factor for crack growth with cathodic polarization (Kth). The hydrogen embrittlement mechanism at the notch for a double-aged microstructure was independent of the loading mode (dynamic straining versus constant displacement holds). For alloy 718 microstructures where no δ phase was present, the hydrogen embrittlement mechanism was similar for under-aged to peak-aged conditions. The presence of δ phase in equivalent strength microstructures significantly increased hydrogen embrittlement susceptibility, and strength level did not correlate strongly to hydrogen sensitivity.

Key words: Precipitation hardened nickel-base alloys, Hydrogen embrittlement, Slow strain rate testing, Incremental step load testing, Rising displacement testing, UNS N07718

The influence of loading mode and specimen geometry on the measured hydrogen embrittlement susceptibility of UNS N07718 (alloy 718) has been assessed. Slow strain rate (SSR) experiments were performed with smooth specimens, while incremental step load (ISL) testing and rising displacement (RD) testing were performed on circular notch tensile (CNT) specimens with cathodic hydrogen charging. Several microstructures of alloy 718 with different strength levels and amounts of grain boundary δ phase precipitation were evaluated. Fracture modes were also evaluated with scanning electron microscopy and correlated to the microstructures and testing methods. Hydrogen embrittlement susceptibilities and fracture modes were similar for each test method and were highly dependent on microstructure. It is interpreted that hydrogen-affected cracking of alloy 718 requires a certain level of plasticity and an adequate amount of absorbed hydrogen in both the SSR test and the accelerated fracture mechanics ISL and RD tests. These criteria are related to the measured threshold stress intensity factor for crack growth with cathodic polarization (Kth). The hydrogen embrittlement mechanism at the notch for a double-aged microstructure was independent of the loading mode (dynamic straining versus constant displacement holds). For alloy 718 microstructures where no δ phase was present, the hydrogen embrittlement mechanism was similar for under-aged to peak-aged conditions. The presence of δ phase in equivalent strength microstructures significantly increased hydrogen embrittlement susceptibility, and strength level did not correlate strongly to hydrogen sensitivity.

Key words: Precipitation hardened nickel-base alloys, Hydrogen embrittlement, Slow strain rate testing, Incremental step load testing, Rising displacement testing, UNS N07718

Also Purchased
Picture for Hydrogen Embrittlement Susceptibility of Precipitation Hardened Ni-Alloys
Available for download

51314-3948-Hydrogen Embrittlement Susceptibility of Precipitation Hardened Ni-Alloys

Product Number: 51314-3948-SG
ISBN: 3948 2014 CP
Author: Carlo Malara
Publication Date: 2014
$0.00
Picture for Evaluation of Susceptibility to Hydrogen Embrittlement of High Strength Corrosion Resistant
Available for download

51316-7847-Evaluation of Susceptibility to Hydrogen Embrittlement of High Strength Corrosion Resistant

Product Number: 51316-7847-SG
ISBN: 7847 2016 CP
Author: Masayuki Sagara
Publication Date: 2016
$20.00