06458 UNDER-DEPOSIT CORROSION MECHANISMS IN BOILERS

Under-deposit corrosion is a common mode of failure in boiler tubes. Mechanisms include phosphate attack, caustic gouging, hydrogen damage, and wall thinning due to metal loss. Many aspects of these mechanisms and their mitigation are well-understood, while certain specific details remain uncertain or subject to controversy.

 

Product Number: 51300-06458-SG
ISBN: 06458 2006 CP
Author: A.G. Howell
$0.00
$20.00
$20.00

Under-deposit corrosion is a common mode of failure in boiler tubes. Mechanisms of corrosion include phosphate attack, caustic gouging, hydrogen damage, and wall thinning due to general metal loss. Many aspects of these mechanisms and their mitigation are well-understood, while certain specific details remain uncertain or subject to controversy.

Keywords: under-deposit corrosion, phosphate corrosion, caustic gouging, hydrogen, damage, boiler tube failures, boiler tube deposits

 

Under-deposit corrosion is a common mode of failure in boiler tubes. Mechanisms of corrosion include phosphate attack, caustic gouging, hydrogen damage, and wall thinning due to general metal loss. Many aspects of these mechanisms and their mitigation are well-understood, while certain specific details remain uncertain or subject to controversy.

Keywords: under-deposit corrosion, phosphate corrosion, caustic gouging, hydrogen, damage, boiler tube failures, boiler tube deposits

 

PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Also Purchased
Picture for 96544 SOME COMMON CORROSION MECHANISMS LEADING
Available for download

96544 SOME COMMON CORROSION MECHANISMS LEADING TO BOILER TUBE FAILURE

Product Number: 51300-96544-SG
ISBN: 96544 1996 CP
Author: D. I. Bain, J. D. Haff, J. A. Kelly
$20.00