03379 IN SITU IMAGING OF CORROSION EVENTS IN AUSTENITIC STEELS BY SCANNING ELECTROCHEMICAL MICROSCOPY

Picture for 03379 IN SITU IMAGING OF CORROSION EVENTS
Available for download
Product Number: 51300-03379-SG
ISBN: 03379 2003 CP
Author: T.E. Lister, R.E. Mizia, and P.J. Pinhero
$0.00
$20.00
$20.00
Scanning electrochemical microscopy (SECM) was used to study the corrosion behavior of 300 Series austenitic steels. Using the substrate generation / tip collection (SG/TC) mode, the I- ion was used as both the aggressive species and the method of detecting oxide breakdown. With the microelectrode tuned to detection of the oxidized product (I3 -), it was brought to within 10 µm of the sample surface. Mapping of the surface showed that current was isolated to discrete locations where pitting corrosion was observed. The SECM maps of the surface followed the expected trend of stability: 316 >> 304L > 304. The 316L sample did not pit in I- solution unless Cl- was added. As a test of the technique, the corrosion of a cross-sectioned 316 weld was imaged. The expected behavior was pitting surrounding the weld due to heat sensitization. The results showed that the base 316 material was contaminated with non-metallic inclusions and showed high activity compared to the filler material which showed no activity. The potential of SECM in studying corrosion was discussed. Keywords: scanning electrochemical microscopy, SECM, stainless steel, 304, 316, pitting corrosion, corrosion mechanism
Scanning electrochemical microscopy (SECM) was used to study the corrosion behavior of 300 Series austenitic steels. Using the substrate generation / tip collection (SG/TC) mode, the I- ion was used as both the aggressive species and the method of detecting oxide breakdown. With the microelectrode tuned to detection of the oxidized product (I3 -), it was brought to within 10 µm of the sample surface. Mapping of the surface showed that current was isolated to discrete locations where pitting corrosion was observed. The SECM maps of the surface followed the expected trend of stability: 316 >> 304L > 304. The 316L sample did not pit in I- solution unless Cl- was added. As a test of the technique, the corrosion of a cross-sectioned 316 weld was imaged. The expected behavior was pitting surrounding the weld due to heat sensitization. The results showed that the base 316 material was contaminated with non-metallic inclusions and showed high activity compared to the filler material which showed no activity. The potential of SECM in studying corrosion was discussed. Keywords: scanning electrochemical microscopy, SECM, stainless steel, 304, 316, pitting corrosion, corrosion mechanism
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 03370 Effect of Vapor Phase Corrosion Inhibitor
Available for download

03370 Effect of Vapor Phase Corrosion Inhibitor (VCI) on the Reliability of Thin Film Inductive Magnetic Recording Heads

Product Number: 51300-03370-SG
ISBN: 03370 2003 CP
Author: Kunigahalli L. Vasanth, Marcia Golub, Herman Pandana and Romel Gomez
$20.00
Picture for 03368 LABORATORY EVALUATION TO CHEMICALLY INHIBIT
Available for download

03368 LABORATORY EVALUATION TO CHEMICALLY INHIBIT HIC AND SSC IN ERW CASING IN BOTH LIQUID AND VAPOR PHASE

Product Number: 51300-03368-SG
ISBN: 03368 2003 CP
Author: M.R. Gregg, G.L Lee
$20.00
Picture for 03376 MAKING CREDIBLE CORROSION MEASUREMENTS-
Available for download

03376 MAKING CREDIBLE CORROSION MEASUREMENTS - REAL CORROSION, REAL TIME

Product Number: 51300-03376-SG
ISBN: 03376 2003 CP
Author: Dawn C. Eden, Michael S. Cayard, Joseph D. Kintz, Robert A .Schrecengost, Bernard P. Breen, Edward K
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support